Extended Planar Defects of Oxygen Vacancies in Ferroelectric BaTiO₃ and Impact on Ferroelectricity

Authors

Shaohui Qiu, University of Arkansas, FayettevilleFollow
Huaxiang Fu, University of Arkansas, FayettevilleFollow

Document Type

Article

Publication Date

11-2023

Keywords

Ferroelectricity; Oxygen vacancy

Abstract

Extended defects of vacancies in ferroelectrics (FE), where vacancies spread over an extended space, are of critical importance in terms of understanding the long-standing problems such as polarization fatigue and aging. However, extended defects in FEs are poorly understood. Here we investigate the extended planar oxygen vacancies in ferroelectric BaTiO₃ using density functional theory and the modern theory of polarization. Oxygen vacancies of different charge states, namely V ²⁺_O , V ¹⁺_O , and V ⁰_O , are studied. We obtain interesting results such as: (i) The formation energy of planar V ²⁺_O vacancies can be very small (merely 0.54 eV) even under the oxygen-rich condition, which is considerably smaller than the formation energy (4.0 eV) of planar V ⁰_O vacancies; (ii) Planar V ²⁺_O vacancies drastically reduce the ferroelectric polarization in BaTiO₃ by more than one order of magnitude, which provides a pivotal (theoretical) evidence that the planar oxygen vacancies could be the origin of polarization fatigue and imprinting. The polarization dead layer caused by planar oxygen vacancies is shown to be around 72 Å. Microscopic origin and insight, based on the local Ti-O relative displacements, are provided to understand these interesting phenomena.

Citation

Qiu, S., & Fu, H. (2023). Extended Planar Defects of Oxygen Vacancies in Ferroelectric BaTiO₃ and Impact on Ferroelectricity. Scientific Reports, 13, 19578. https://doi.org/10.1038/s41598-023-46489-y

Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.